Performance of Biocarbon based Electrodes for Electrochemical Capacitor

Syarif, Nirwan (2014) Performance of Biocarbon based Electrodes for Electrochemical Capacitor. Energy Procedia, 52. pp. 18-25.

[img]
Preview
PDF - Published Version
Download (603Kb) | Preview

    Abstract

    We examined bio-carbon electrodes-based electrochemical capacitor. The electrodes were produced from gelam wood activated carbon. Six types of carbon electrodes in separator – electrodes assemblies were tested using galvanostatic charging – discharging (GCD) and electrochemical impedance spectroscopy (EIS) instrumentation. Eight types of aqueous solution from acid, base and salt were used as electrolytes. Three of six electrodes were prepared from carbon pellet sand others were prepared from powdered carbons. Carbon pellets were shaped and sized into electrode monoliths, and therefore those pellets were becoming binder-less. The powdered carbon were compacted along with binder and surfactant into 20 mm in diameter electrodes. The GCD and EIS measurements clearly indicated that both binderless and binderized carbon electrodes (CE) in electrochemical capacitor (EC) have 0.01 – 28 Fg-1 and 0.001 – 2.8 Fg-1 of specific capacitance, respectively. Performance tests of EC measured with EIS and GCD methods respectively have 0.001 – 0.15 F and 0.001 – 0.203 F of capacitance.

    Item Type: Article
    Subjects: Q Science > QD Chemistry
    T Technology > TP Chemical technology
    Divisions: Faculty of Mathematics and Natural Sciences > Department of Chemistry
    Depositing User: Dr Nirwan Syarif
    Date Deposited: 28 Dec 2017 14:49
    Last Modified: 28 Dec 2017 14:49
    URI: http://eprints.unsri.ac.id/id/eprint/7571

    Actions (login required)

    View Item