Performance Evaluation of uncoated and TiCN coated Carbide Tools when End Milling of Titanium Alloy Ti-6Al-4V

Mohruni, Amrifan Saladin (2005) Performance Evaluation of uncoated and TiCN coated Carbide Tools when End Milling of Titanium Alloy Ti-6Al-4V. Proceeding of The 8th International Conference on Quality in Research University of Indonesia, Faculty of Engineering, ME15-M (MPSDO-). Faculty of Engineering, University of Indonesia, Jakarta, Indonesia, pp. 1-5. ISBN ISSN-1411-1284

WarningThere is a more recent version of this item available.
PDF (QIR UI 2005) - Published Version
Download (269Kb) | Preview


    Cutting performance of uncoated WC/Co and TiCN coated solid carbide tools when end milling titanium alloy, Ti-6Al-4V was carried out investigated. Tool wear, tool life and cutting forces were investigated during end milling at various cutting speeds. Results showed that uncoated endmill outperformed TiCN coated endmill with regards to tool life at cutting speeds 130 m/min and below. However TiCN coated tools was more superior when endmilling at higher cutting speed. Both tools suffered nonuniform flank wear and chipping at the main cutting edge at most cutting conditions. In general, cutting force was slightly higher when machining with TiCN tool as compared to the uncoated tool. Similar trend of decreasing cutting force with increasing cutting speed was observed on both tools. At higher cutting speed, the effect of TiCN coatings on the cutting force was not significant when the difference in cutting force was very marginal between both tools. Keywords—Cutting Force, End Milling, Tool Life, Titanium Alloy, Tool Wear.

    Item Type: Book
    Subjects: T Technology > TJ Mechanical engineering and machinery
    T Technology > TS Manufactures
    Divisions: Faculty of Engineering > Department of Mechanical Engineering
    Depositing User: Dipl.-Ing. Ir. PhD. Amrifan Saladin Mohruni
    Date Deposited: 06 Apr 2016 11:26
    Last Modified: 06 Apr 2016 11:26

    Available Versions of this Item

    Actions (login required)

    View Item